Low-temperature approach to highly emissive copper indium sulfide colloidal nanocrystals and their bioimaging...

We report our newly developed low-temperature synthesis of colloidal photoluminescent (PL) CuInS2 nanocrystals (NCs) and their in vitro and in vivo imaging applications. With diphenylphosphine sulphide (SDPP) as a S precursor made from elemental S and diphenylphosphine, this is a noninjection based approach in 1-dodecanethiol (DDT) with excellent synthetic reproducibility and large-scale capability. For a typical synthesis with copper iodide (CuI) as a Cu source and indium acetate (In(OAc)3) as an In source, the growth temperature was as low as 160 °C and the feed molar ratios were 1Cu-to-1In-to-4S. Amazingly, the resulting CuInS2 NCs in toluene exhibit quantum yield (QY) of ~23% with photoemission peaking at ~760 nm and full width at half maximum (FWHM) of ~140 nm. With a mean size of ~3.4 nm (measured from the vertices to the bases of the pyramids), they are pyramidal in shape with a crystal structure of tetragonal chalcopyrite. In situ (31)P NMR (monitored from 30 °C to 100 °C) and in situ absorption at 80 °C suggested that the Cu precursor should be less reactive toward SDPP than the In precursor. For our in vitro and in vivo imaging applications, CuInS2/ZnS core-shell QDs were synthesized; afterwards, dihydrolipoic acid (DHLA) or 11-mercaptoundecanoic acid (MUA) were used for ligand exchange and then bio-conjugation was performed. Two single-domain antibodies (sdAbs) were used. One was 2A3 for in vitro imaging of BxPC3 pancreatic cancer cells. The other was EG2 for in vivo imaging of a Glioblastoma U87MG brain tumour model. The bioimaging data illustrate that the CuInS2 NCs from our SDPP-based low-temperature noninjection approach are good quality.