Flexural strength and degree of polymerization of a proprietary denture base acrylic resin designed to be cured using

Related Experiment Video

Updated: May 13, 2026

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
03:02

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins

Published on: January 17, 2025

H A Bentaher, A S Juszczyk, S Deb

    The European Journal of Prosthodontics and Restorative Dentistry
    |March 19, 2013
    PubMed

    More Related Videos

    Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

    Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

    Published on: December 20, 2024

    Related Concept Videos

    Polymer Classification: Architecture01:14

    Polymer Classification: Architecture

    Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
    Classification and Mechanical Properties of Synthetic Polymers01:28

    Classification and Mechanical Properties of Synthetic Polymers

    Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...
    Polymer Classification: Stereospecificity01:26

    Polymer Classification: Stereospecificity

    Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
    Step-Growth Polymerization: Overview01:03

    Step-Growth Polymerization: Overview

    Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
    Many natural and synthetic polymers are produced by...
    Accelerated Curing of Concrete01:25

    Accelerated Curing of Concrete

    Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...