Plastic damage induced fracture behaviors of dental ceramic layer structures subjected to monotonic load

Raorao Wang1, Chenglin Lu, Dwayne Arola

  • 1The Tenth People's Hospital of Tongji University, Shanghai, PR China.

Journal of Prosthodontics : Official Journal of the American College of Prosthodontists
|April 5, 2013
PubMed
Abstract

Keywords:
DICceramic crownscrackfracturemonotonic loaddental ceramicsfracture mechanicsmonotonic load testingzirconia core

More Related Videos

In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint07:09

In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint

Published on: March 7, 2014

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

Related Concept Videos

Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and reloaded.
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
Plastic Deformations01:19

Plastic Deformations

Plastic deformation represents a fundamental concept in materials science, which explains the irreversible change in the shape of a material when it experiences stress beyond its elastic capability. This phenomenon is important in structural engineering, especially in designing and analyzing cantilever beams—structures that are securely fixed at one end and bear loads at the opposite end. When these beams are subjected to loads within their elastic range, they will return to their original...
Plastic Deformations01:14

Plastic Deformations

It is essential to understand how structural members behave under plastic deformation when the bending stress exceeds the material's yield strength. This state of deformation permanently alters the shape of the member, in contrast to the linear elastic behavior observed before yielding. The strain at any point in the member is expressed in terms of maximum strain. Notably, the neutral axis, which coincides with the centroid during elastic bending, shifts away from the centroid under plastic...
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...