Enhanced microwave absorbing performance of CoNi alloy nanoparticles anchored on a spherical carbon monolith
Na Li1, Changwen Hu, Minhua Cao
1Key Laboratory of Cluster Science, Ministry of Education of China, Department of Chemistry, Beijing Institute of Technology, Beijing 100081, PR China.
Abstract:
CoNi alloy nanoparticles anchored on a spherical carbon monolith (CoNi-C) were prepared by a solvothermal route and subsequent heat treatment without any templates. Their permittivity and permeability behaviors were studied in the frequency range of 2-18 GHz. The CoNi-C composites showed the best microwave absorbing performances compared to those of Co-C and Ni-C. The maximum reflection loss of the CoNi-C nanocomposites can reach -50.2 dB at 7.7 GHz with samples of 4 mm in thickness, better than that of the Ni-C composites, while the Co-C composites showed almost no absorption at all. The absorption mechanism of the three absorbents was also discussed.
More Related Videos
09:20Microhoneycomb Monoliths Prepared by the Unidirectional Freeze-drying of Cellulose Nanofiber Based Sols: Method and Extensions
Published on: May 24, 2018
07:47Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles
Published on: November 27, 2015