Fast incorporation of primary amine group into polylactide surface for improving C₂C₁₂ cell proliferation using...

In this article, we report the development of the fast incorporation of primary amine functional groups into a polylactide (PLA) surface using the post-discharge jet region of an atmospheric-pressure nitrogen-based dielectric barrier discharge (DBD). Plasma treatments were carried out in two sequential steps: (1) nitrogen with 0.1% oxygen addition, and (2) nitrogen with 5% ammonia addition. The analyses show that the concentration of N/C ratio, surface energy, contact angle, and surface roughness of the treated PLA surface can reach 19.1%, 70.5 mJ/m(2), 38° and 73.22 nm, respectively. In addition, the proposed two-step plasma treatment procedure can produce a PLA surface exhibiting almost the same C2C12 cell attachment and proliferation performance as that of the conventional gelatin coating method. Most importantly, the processing/preparation time is reduced from 13-15 h (gelatin coating method) to 5-15 min (two-step plasma treatment), which is very useful in practical applications.