Color metallography and electron microscopy techniques applied to the characterization of 413.0 aluminum alloys

The influence on alloy 413.0 of the refinement and modification of its microstructure was analyzed by means of several microscopy techniques, as well as the effect of the application of high pressure during solidification. For each treatment and solidification pressure condition employed, the most suitable microscopy techniques for identifying and characterizing the phases present were investigated. Color metallography and electron microscopy techniques were applied to the qualitative microstructural analysis. Volume fraction and grain size of the primary α-Al were characterized by quantitative metallographic techniques. The results show that the effect caused by applying high pressure during solidification of the alloy is more pronounced than that caused by modification and refinement of the microstructure when it solidifies at atmospheric pressure. Furthermore, it has been shown that, for Al-Si alloy characterization, when aiming to characterize the primary α-Al phase, optical color metallography observed under crossed polarized light plus a sensitive tint filter is the most suitable technique. When the goal is to characterize the eutectic Si, the use of optical color metallography or electron microscopy is equally valid. The characterization of iron-rich intermetallic compounds should preferably be performed by means of backscattered electron imaging.