Mesenchymal stem cell proliferation and differentiation on load-bearing trabecular Nitinol scaffolds

Bone tissue regeneration in load-bearing regions of the body requires high-strength porous scaffolds capable of supporting angiogenesis and osteogenesis. 70% porous Nitinol (NiTi) scaffolds with a regular 3-D architecture resembling trabecular bone were produced from Ni foams using an original reactive vapor infiltration technique. The "trabecular Nitinol" scaffolds possessed a high compressive strength of 79 MPa and high permeability of 6.9×10(-6) cm2. The scaffolds were further modified to produce a near Ni-free surface layer and evaluated in terms of Ni ion release and human mesenchymal stem cell (hMSC) proliferation (AlamarBlue), differentiation (alkaline phosphatase activity, ALP) and mineralization (Alizarin Red S staining). Scanning electron microscopy was employed to qualitatively corroborate the results. hMSCs were able to adhere and proliferate on both as-produced and surface-modified trabecular NiTi scaffolds, to acquire an osteoblastic phenotype and produce a mineralized extracellular matrix. Both ALP activity and mineralization were increased on porous scaffolds compared to control polystyrene plates. Experiments in a model coculture system of microvascular endothelial cells and hMSCs demonstrated the formation of prevascular structures in trabecular NiTi scaffolds. These data suggest that load-bearing trabecular Nitinol scaffolds could be effective in regenerating damaged or lost bone tissue.