Mössbauer and magnetic studies of surfactant mediated Ca-Mg doped ferrihydrite nanoparticles

Ultrafine (2-5 nm) particles of amorphous Ca-Mg co-doped ferrihydrite have been synthesized by surfactant mediated co-precipitation method. The evolution of the amorphous ferrihydrite by Ca-Mg co-doping is quite different from our earlier investigations on individual doping of Ca and Mg. Amorphous phase of ferrihydrite for the present study has been confirmed by X-ray diffraction (XRD) and Mössbauer spectroscopy at room temperature and low temperatures (40 K and 20 K). Hematite nanoparticles with crystallite size about 8, 38 and 70 nm were obtained after annealing the as-prepared samples at 400, 600 and 800 degrees C respectively in air atmosphere. Superparamagnetism has been found in 8 nm sized hematite nanoparticles which has been confirmed from the magnetic hysteresis loop with zero remanent magnetization and coercive field and also from the superparamagnetic doublet of its room temperature Mössbauer spectrum. The magnetic properties of the 38 and 70 nm sized particles have been studied by room temperature magnetic hysteresis loop measurements and Mössbauer spectroscopy. The coercive field in these hematite nanoparticles increases with increasing particle size. Small amount of spinel MgFe2O4 phase has been detected in the 800 degrees C annealed sample.