Preparation of anatase/rutile mixed-phase titania nanoparticles for dye-sensitized solar cells

Acid-labile high surface mesoporous ZnO/Zn(OH)2 composite material is used as a novel hard template for the preparation of mesoporous amorphous TiO2. The template-free amorphous TiO2 material is then thermally crystallized at suitable temperature to control the relative ratio of anatase and rutile phases in a particle. Four different anatase/rutile (AR) mixed-phase TiO2 nanoparticles (AR-3, AR-15, AR-20, and AR-23 denoted for the samples of 3%, 15%, 20%, and 23% rutile phase, respectively) are prepared and characterized by powder X-ray diffraction (PXRD) and transmission electron microscopy (TEM). The coexistence of anatase and rutile phases in a TiO2 nanoparticle is visually confirmed by HRTEM analysis. These mixed-phase TiO2 nanoparticles are examined as candidates for photoelectrodes of dye-sensitized solar cells (DSSCs). The J-V curves and IPCE spectra for the DSSCs prepared from the mixed-phase TiO2 nanoparticles are obtained, and their photovoltaic properties are investigated. The photo-conversion efficiency (eta) indicates the highest value of 5.07% for AR-20. The synergistic effect of coexisting anatase and rutile phases with an optimal ratio in a TiO2 nanoparticle of AR-20 for an efficient interfacial transfer of photo-generated electrons is likely to lead to the highest efficiency among the AR-n samples.