Effect of opacifiers and UV absorbers on pigmented maxillofacial silicone elastomer, part 1: color stability after
Ying Han1, John M Powers, Sudarat Kiat-Amnuay
1Department of Prosthodontics, School of Stomatology, Fourth Military Medical University, Xi'an, China.
Statement Of Problem:
Much dissatisfaction with the color instability and reduced lifetime of extraoral maxillofacial prostheses due to degradation has been reported.
Purpose:
The purpose of this study was to compare the effect of a UV mineral-based light protecting agent (LP) on the color stability of pigmented maxillofacial silicone elastomer MDX-4210/Type A after artificial aging to 2 widely used opacifiers.
Material And Methods:
Forty-five groups were established (n=225 total). Three different types of opacifiers (LP, titanium white dry pigment [TW], or silicone intrinsic white [SW]) were added to silicone MDX-4210/type A at 3 concentrations (5%, 10%, or 15%) and subsequently combined with each of 5 colors (no pigments [control], red, blue, yellow, or mixed pigments). Artists' oil pigment was used with LP and TW, while intrinsic silicone pigment was used to color SW. Before and after an energy exposure of 450 kJ/m(2), CIE L*a*b* values were measured with a spectrophotometer. The CIELAB 50:50% perceptibility (ΔE*=1.1) and acceptability threshold (ΔE*=3.0) were used to interpret color changes (ΔE*). Color differences after aging were subjected to 3-way ANOVA. Means were compared by the Fisher PLSD intervals at α=.05.
Results:
The ΔE* values of all groups were below the acceptability threshold of ΔE*=3.0, except for the control group of SW at 10%, which showed the greatest color change (ΔE*=3.1). When mixed pigment groups were considered, at 5% concentration, LP showed the smallest color change, followed by SW and TW (P<.05); at 10%, no significant differences among the 3 opacifiers were noted (P>.05); at 15%, LP showed the smallest color change, followed by TW and SW (P<.05).
Conclusions:
All 3 opacifiers at all concentrations protected pigmented silicone MDX4-4210/Type A from color degradation. The LP group showed the smallest color changes.