Preparation and properties of Starch-g-PLA/poly(vinyl alcohol) composite film

Starch/lactic acid graft copolymer (Starch-g-PLA) was prepared by the in situ copolymerization of starch grafted with lactic acid catalyzed with sodium hydroxide, and then mixed with poly(vinyl alcohol) (PVA) to get composite films. The structures of the graft copolymer and composite films were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties, water resistance, and thermal stability were also investigated. It was found that the compatibility of Starch-g-PLA and PVA was better than that of starch and PVA in the composite films. The tensile strength and elongation at break of the Starch-g-PLA/PVA composite film increased by 69.15% and 84.22%, respectively, while the water absorption decreased by 50.39%, which overcame the shortcomings of hydrophilicity and poor mechanical properties of Starch/PVA film. Thermogravimetric analysis (TGA) also showed that the thermal stability of Starch-g-PLA/PVA film was improved compared with Starch/PVA film.