Control of crystal morphology in monodisperse polyfluorenes by solvent and molecular weight

Chengfang Liu1, Qilin Wang, Hongkun Tian

  • 1State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, PR China.

The Journal of Physical Chemistry. B
|July 4, 2013
PubMed

More Related Videos

Controlled Synthesis and Fluorescence Tracking of Highly Uniform Poly(N-isopropylacrylamide) Microgels11:34

Controlled Synthesis and Fluorescence Tracking of Highly Uniform Poly(N-isopropylacrylamide) Microgels

Published on: September 8, 2016

Controlling the Size, Shape and Stability of Supramolecular Polymers in Water16:24

Controlling the Size, Shape and Stability of Supramolecular Polymers in Water

Published on: August 2, 2012

Related Concept Videos

Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
Determination of Molar Masses of Polymers I01:24

Determination of Molar Masses of Polymers I

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.
Polymers: Defining Molecular Weight01:01

Polymers: Defining Molecular Weight

Unlike small molecules with definite molecular weights, polymers are a mixture of individual polymer chains of varying lengths, each with a unique molecular weight. So, the molecular weight of a polymer is expressed as an average value based on the average size of the polymer chains. The two most common forms of averages used for polymers are the number average molecular weight and weight average molecular weight.
The number average molecular weight (Mn) is the summation of the number...
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...