Nano magnetic solid phase extraction for preconcentration of lead ions in environmental samples by a newly...

In this study, magnetite nanoparticles with particle size lower than 47 nm were synthesized and were applied for preconcentration of Pb2+ ions from aqueous solutions. To preconcentrate the Pb2+ ions, the surface of the synthesized nano particles was modified with sodium dodecyl sulfate (SDS) as an anionic surfactant. A new chelating agent (2-((E)-2-amino-4,5-dinitrophenylimino)methyl)phenol) was synthesized and used to form a very stable complex with Pb2+ ions. The lead ions formed complexes and were quantitatively extracted with SDS-coated magnetite nanoparticles. After magnetic separation of adsorbent, the adsorbent was eluted with 0.5% (v/v) HC1 in dimethyl sulfoxide (DMSO) prior to analysis by flame atomic absorption spectrometry (FAAS). Orthogonal array design (OAD) was used to study and optimize the different experimental parameters. Under the optimum conditions, enhancement factor up to 63.5 was achieved for extraction from only 10 mL of sample solution and the relative standard deviation (RSD %) of the method was lower than 2.8%. The obtained calibration curve was linear in the range of 1-300 pg L-' with reasonable linearity (r2 > 0.998). The limit of detection (LOD) based on S/N = 3 was 0.04 microg L(-1) for 10 mL sample volumes. Finally, applicability of the proposed method was successfully confirmed by preconcentration and determination of trace amounts of lead ions in environmental samples and satisfactory results were obtained.