Biological Compatibility Profile on Biomaterials for Bone Regeneration
10:28

Biological Compatibility Profile on Biomaterials for Bone Regeneration

Published on: November 16, 2018

Chemical and physical properties of bone cement for vertebroplasty

Po-Liang Lai1, Lih-Hui Chen, Wen-Jer Chen

  • 1Department of Orthopaedic Surgery, Chang Gung Memorial Hospital at Linkou, Chang Gung University College of Medicine, Taoyuan, Taiwan. polianglai@gmail.com

Biomedical Journal
|August 31, 2013
PubMed

More Related Videos

Comprehensive Characterization of Tissue Mineralization in an Ex Vivo Model07:29

Comprehensive Characterization of Tissue Mineralization in an Ex Vivo Model

Published on: September 27, 2024

Related Concept Videos

Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to the...
Bone Remodeling01:40

Bone Remodeling

Bone remodeling is a continuous and balanced process of bone resorption by osteoclasts and bone formation by osteoblasts. In adults, it helps maintain bone mass and calcium homeostasis. While mechanical stress can stimulate turnover as part of the normal maintenance and reparative process, several hormones also regulate bone remodeling.
The Bone Matrix01:18

The Bone Matrix

Bone contains a relatively small number of cells entrenched in a matrix of collagen fibers that provide an adherent surface for inorganic salt crystals. Both components of the matrix, organic and inorganic, contribute to the unusual properties of bone. Without collagen, bones would be brittle and shatter easily. Without mineral crystals, bones would flex and provide little support. This can be observed by an experiment: when the minerals of a bone are dissolved by soaking the bone in acid or...
Bone as Supporting Connective Tissue01:23

Bone as Supporting Connective Tissue

Bone tissue forms the internal skeleton of vertebrate animals, providing structure to the body.
Bone Matrix
Bone, or osseous tissue, is a connective tissue that has a large amount of two different types of matrix material. The organic matrix is similar to the matrix material found in other connective tissues, including some amount of collagen and elastic fibers. This gives strength and flexibility to the tissue. The inorganic matrix consists of mineral salts— mostly calcium salts— that give the...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...