Antifungal effect of calcium enriched mixture cement against Candida albicans

Ali Kangarlou1, Samira Sofiabadi, Zahra Yadegari

  • 1Department of Endodontics, Iranian Center for Endodontic Research, Dental School, Shahid Beheshti University of Medical Sciences, Tehran, Iran.

Iranian Endodontic Journal
|September 5, 2013
PubMed
Abstract

Keywords:
CEM cementCandida AlbicansMTANECRoot-end filling

More Related Videos

A Soluble Tetrazolium-Based Reduction Assay to Evaluate the Effect of Antibodies on Candida tropicalis Biofilms06:50

A Soluble Tetrazolium-Based Reduction Assay to Evaluate the Effect of Antibodies on Candida tropicalis Biofilms

Published on: September 16, 2022

Candida albicans Biofilm Chip (CaBChip) for High-throughput Antifungal Drug Screening08:05

Candida albicans Biofilm Chip (CaBChip) for High-throughput Antifungal Drug Screening

Published on: July 18, 2012

Related Concept Videos

Antifungal Agents01:15

Antifungal Agents

Amphotericin B is a broad-spectrum antifungal agent that exploits structural differences between fungal and mammalian cell membranes. Its amphipathic structure—featuring a hydrophobic polyene-lactone ring and a hydrophilic region containing mycosamine and carboxylic acid groups—enables selective binding to ergosterol, a sterol predominantly found in fungal plasma membranes. This selective interaction underlies the drug’s antifungal activity, although weak binding to cholesterol contributes to...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Fineness of Cement01:15

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
Waterproofing and Anti-Bacterial Admixtures in Concrete01:22

Waterproofing and Anti-Bacterial Admixtures in Concrete

Concrete's susceptibility to water absorption is due to the capillary action within the pores of its hydrated cement paste. This action draws water in, creating the need for waterproofing admixtures to prevent such penetration. The efficacy of these admixtures is contingent upon the water pressure, with variations arising from different conditions such as rain, capillary rise, or hydrostatic pressure in structures intended to hold water.
Waterproofing admixtures render concrete hydrophobic,...
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...