Note: Effects of polydispersity on the phase behavior of AB diblock and BAB triblock copolymer melts: A dissipative...

Copolymers are the products obtained from the polymerization of multiple monomer species. So, in a polymer chain itself, there can be multiple repeating units that come from different monomers. The process of synthesizing a polymer from different monomer species is called copolymerization. When two monomers are involved, the polymer is known as a bipolymer. Polymers with three and four monomers are termed terpolymers and quaterpolymers, respectively. Figure 1 depicts the copolymerization of...

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...