A novel approach for FE-SEM imaging of wood-matrix polymer interface in a biocomposite

Understanding the interface between polymer and biomass in composite products is important for developing high performance products, as the quality of adhesion at the interface determines composite properties. For example, with greater stiffness compared to polymer matrix, such as that of high density polyethylene, the wood component enhances stiffness of wood-polymer composites, provided there is good adhesion between composite components. However, in composites made from wood flour (wood particles) and synthetic resins it is often difficult to clearly resolve particle-matrix interfaces in the conventionally employed microscopy method that involves SEM examination of fractured faces of composites. We developed a novel approach, where composites made from high density polyethylene and wood flour were examined and imaged with a FE-SEM (field emission scanning electron microscope) in transverse sections cut through the composites. Improved definition of the interface was achieved using this approach, which enabled a more thorough comparison to be made of the features of the interface between wood particles and the matrix in composites with and without a coupling agent, as it was possible to clearly resolve the interfaces for particles of all sizes, from large particles consisting of many cells down to tiny cell wall fragments, particularly in composites that did not incorporate the coupling agent used to enhance particle adhesion with the matrix polymer. The method developed would be suitable particularly for high definition SEM imaging of a wide range of composites made combining wood and agricultural residues with synthetic polymers.