Size dependent reduction-oxidation-reduction behaviour of cobalt oxide nanocrystals

Morphologically similar cobalt oxide nanoparticles (Co3O4) of four different sizes (3 nm, 6 nm, 11 nm and 29 nm) with narrow size distribution were prepared by subtle variation of synthesis conditions. These nanoparticles were used as model materials to understand the structural and morphological changes that occur to cobalt oxide during sequential reduction, oxidation and further re-reduction process as a function of the initial size of cobalt oxide. On reduction, spherical cobalt nanoparticles were obtained independent of the original size of cobalt oxide. In contrast, subsequent oxidation of the metal particles led to solid spheres, hollow spheres or core-shell structures depending on the size of the initial metal particle. Further re-reduction of the oxidized structures was also observed to be size dependent. The hollow oxide shells formed by the large particles (29 nm) fragmented into smaller particles on reduction, while the hollow shells of the medium sized particles (11 nm) did not re-disperse on further reduction. Similarly, no re-dispersion was observed in the case of the small particles (6 nm). This model study provides useful insights into the size dependent behavior of metal/metal oxide particles during oxidation/reduction. This has important implications in petrochemical industry where cobalt is used as a catalyst in the Fischer-Tropsch process.