Evora® chromium-cobalt dual mobility socket: results at a minimum 10 years' follow-up

The Evora chromium-cobalt alloy dual mobility socket claims to display a large articulation tribology different from that of stainless steel models, limiting the risk of intraprosthetic dislocation and wear. The present study reports a minimum of 10years' follow-up in a multicenter prospective series of 200 sockets previously reported on at 5years.

The use of chromium-cobalt in dual mobility sockets provides a low rate of failure at 10years, especially as regards to osteolysis and intraprosthetic dislocation.

Two hundred hydroxyapatite-coated molded chromium-cobalt sockets without titanium interface were implanted without cement in 194 patients with a mean age of 70 years (range, 32-91 years). Clinical results were assessed on Postel Merle d'Aubigné and Harris scores, plain radiographs and survival analysis.

At a mean 11 years' follow-up (10-13 years), 56 patients had died and 31 were lost to follow-up. Four underwent surgical revision (3 femoral components, and 1 socket for migration at 9 years with complete disappearance of the hydroxyapatite). A total of 109 implants were analyzable in 107 patients with a mean age of 81 years (55-93 years). At follow-up, the mean Harris score was 90 (75-96) and the PMA score 16.3 (14-18). There were no cases of loosening (except for the case reoperated on at 9 years) and no acetabular radiolucency or cysts. There were 2 cases of non-evolutive femoral radiolucency and 10 of femoral granuloma, involving head size > 22 mm (P<0.0001) and a cemented titanium stem (P=0.004) as risk factors. There were no dislocations in the large or small articulation. Ten-year survival was 99% (95% CI: 97.3%-100%) with socket revision as censorship criterion.

The absence of dislocation in both small and large articulations confirmed the efficacy of the dual mobility concept and suggested an advantage for chromium-cobalt sockets in reducing the rate of intraprosthetic dislocation and preventing blockage of the large articulation by a better performance in the friction couple. Granulomas were associated with wear in cemented titanium stems and with heads greater than 22 mm in diameter. Ten-year survival was 99% (censorship criterion: revision for socket failure); there was, however, one case of socket loosening with disappearance of the hydroxyapatite, indicating that surveillance should be continued in this cohort.