Long-term chlorhexidine effect on bond strength to Er:YAG laser irradiated-dentin

This study evaluates the bond strength of dentin prepared with Er:YAG laser or bur, after rewetting with chlorhexidine on long-term artificial saliva storage and thermocycling. One hundred and twenty human third molars were sectioned in order to expose the dentin surface (n = 10). The specimens were randomly divided in 12 groups according to treatment and aging: Er:YAG laser rewetting with deionized water (LW) and 24 h storage in artificial saliva (WC); LW and 6 months of artificial saliva storage + 12.000 thermocycling (6M), LW and 12 months of artificial saliva storage + 24.000 thermocycling (12M), Er:YAG laser rewetting with 2% chlorhexidine (LC) and WC, LC and 6M, LC and 12M, bur on high-speed turbine rewetting with deionized water (TW) and WC, TW6M, TW12M, bur on high-speed turbine + 2% chlorhexidine (TC) and WC, TC and 6M, TC and 12M. The specimens were etched with 35% phosphoric acid, washed, and dried with air. Single Bond 2 adhesive was applied and the samples were restored with a composite. Each tooth was sectioned in order to obtain 4 sticks, which were submitted to microtensile bond strength test (µTBS). The two-way ANOVA, showed no significant differences for the interaction between the factors and for the aging factor. Tukey 5% showed that the LC group had the lowest µTBS. The rewetting with chlorhexidine negatively influenced the bond strength of the preparation with the Er:YAG laser. The artificial saliva aging and thermocycling did not interfere with dentin bond strength.