Role of the sample thickness in planar crack propagation

Pallab Barai1, Phani K V V Nukala, Mikko J Alava

  • 1Department of Mechanical Engineering, Texas A & M University, College Station, Texas 77843, USA.

Physical Review. E, Statistical, Nonlinear, and Soft Matter Physics
|November 16, 2013
PubMed

More Related Videos

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation05:30

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation

Published on: September 29, 2019

8.5K
Mechanoluminescent Visualization of Crack Propagation for Joint Evaluation04:58

Mechanoluminescent Visualization of Crack Propagation for Joint Evaluation

Published on: January 6, 2023

6.1K

Related Concept Videos

Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
618
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen...
1.7K
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
953
Types of Non-structural Cracks in Concrete01:28

Types of Non-structural Cracks in Concrete

Non-structural cracks are primarily of three types: plastic, early-age thermal, and drying shrinkage cracks. Plastic cracks are further classified into plastic shrinkage cracks and plastic settlement cracks.
Plastic shrinkage cracks typically form within hours after the concrete is poured. The concrete's surface dries faster than the bottom, creating tensile stress that the still-plastic concrete cannot withstand, leading to diagonal or randomly patterned cracks on the concrete surface.
672
X-ray Diffraction of Biological Samples01:10

X-ray Diffraction of Biological Samples

X-ray diffraction or XRD is an analytical tool that utilizes X-rays to study ordered structures such as crystalline organic and inorganic samples, polycrystalline materials, proteins, carbohydrates, and drugs.
According to Bragg's law, when X-rays strike the sample positioned on a stage, the rays are  scattered by the electron clouds around the sample atoms. The  X-ray diffraction or scattering is caused by constructive interference of the X-ray waves that reflect off the internal...
3.9K
Deformations in a Transverse Cross Section01:21

Deformations in a Transverse Cross Section

When a material is subjected to uniaxial stress, it elongates or contracts in the direction of the applied force, and also undergoes changes in the perpendicular directions. This behavior is crucial for understanding how materials behave under stress and is governed by mechanical properties such as Poisson's ratio v, which measures the ratio of transverse strain to axial strain.
As the material stretches, it expands or contracts in orthogonal directions to the load. This phenomenon varies...
718