Fabrication of biocompatible hydrogel coatings for implantable medical devices using Fenton-type reaction

In this paper the authors present a simple method of coating polyurethane (PU) surface with poly(vinyl pirrolidone) (PVP) hydrogel. The hydrogel-coated materials were designed for use in biomedical applications, especially in blood-contacting devices. The coating is formed due to free radical macromolecular grafting-crosslinking. Polymer surface was first immersed in an organic solution containing radical source: cumene hydroperoxide (CHP) with an addition of a branching and anchoring agent: ethylene glycol dimethylacrylate (EGDMA). In the second step, the substrate was immersed in a water solution containing given concentration of PVP and Fe(2+). The novelty of the process consists in the fact that free radicals are formed mostly at the polymer/solution interface, what assures high grafting efficiency together with the formation of covalent bonds between polymer substrate and modifying layer. The process was optimized for reagents concentrations. The coating properties: thickness and the swelling ratio were strongly influenced by CHP, Fe(2+), PVP and EGMDA concentrations. The chemical composition of the surface analyzed with FTIR-ATR spectroscopy confirmed the presence of PVP coating. In vitro biocompatibility tests with L929 fibroblasts confirmed non-cytotoxicity of the coatings. Hydrogel coating significantly improved polyurethane hemocompatibility. Studies with human whole blood revealed that both, the platelet consumption and the level of platelet activation were as low as for negative control.