Structural and electrical properties of microwave processed Ag modified KNN-LS ceramics

Microwave processing steps of 0.95[(K0.5Na0.5)0.94Ag0.06NbO3]-0.05[LiSbO3]/(KNAN-LS) lead free ferroelectric ceramics were optimized for better densification and electrical properties. Calcination temperature and time for single perovskite phase formation were optimized and found to be 850 degrees C for 60 min., respectively. Crystal structural study revealed the presence of mixed structure in the microwave processed (MWP) KNAN-LS ceramics. The sintering of the KNAN-LS ceramics was carried out at 1080 degrees C for 10 min, 20 min and 30 min, respectively, and the sample sintered for 20 min exhibited best properties.