A comparison of the shear bond strength and failure mode to metals of unsupported and supported luting cement

Related Experiment Video

Updated: May 3, 2026

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

955

Joshua J Cheetham, Joseph E Palamara, Martin J Tyas

    The Journal of Adhesive Dentistry
    |January 31, 2014
    PubMed
    Abstract

    More Related Videos

    Mechanoluminescent Visualization of Crack Propagation for Joint Evaluation04:58

    Mechanoluminescent Visualization of Crack Propagation for Joint Evaluation

    Published on: January 6, 2023

    6.1K
    Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives08:40

    Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

    Published on: May 17, 2020

    2.9K

    Related Concept Videos

    Strength of Cement01:20

    Strength of Cement

    Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
    For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
    910
    Bonding and Strength of Aggregate01:12

    Bonding and Strength of Aggregate

    The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
    1.2K
    Tensile Strength Considerations of Concrete01:16

    Tensile Strength Considerations of Concrete

    Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
    The dimensions and shape of a concrete specimen...
    1.7K
    Yield Criteria for Ductile Materials under Plane Stress01:25

    Yield Criteria for Ductile Materials under Plane Stress

    In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
    The Maximum Shearing Stress Criterion, also known as...
    836
    Stress-Strain Diagram - Brittle Materials01:24

    Stress-Strain Diagram - Brittle Materials

    Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
    4.5K
    Soundness of Cement01:17

    Soundness of Cement

    The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...
    744