Zinc induces apatite and scholzite formation during dentin remineralization

The aim of this study was to ascertain whether zinc may improve the repair ability of demineralized dentin. Dentin disks were demineralized by phosphoric acid during 15 s and immersed in artificial saliva, remineralizing solution, a zinc chloride solution and a zinc oxide solution. Dentin specimens were analyzed after 24 h and 1 month of storage. Surface morphology was assessed by atomic force and scanning electron microscopy, mechanical properties were analyzed by nanohardness testing in a TriboIndenter, and chemical changes at the surfaces were determined by X-ray diffraction, Raman and energy-dispersive elemental analyses. After phosphoric acid application, dentin was only partially demineralized. Demineralized dentin was remineralized after 24 h of storage in any of the tested solutions (nanohardness increased and hydroxylapatite formation was detected by Raman). Remineralization was maintained up to 1 month in dentin stored in remineralizing solution, zinc chloride and zinc oxide. Zinc and phosphate were important for hydroxylapatite homeostasis. Scholzite formation was encountered in dentin stored in zinc-containing solutions. Zinc might allow to reach the balance between dentin demineralization and remineralization processes.