Transmittance enhancement of sapphires with antireflective subwavelength grating patterned UV polymer surface...

We report the total and diffuse transmission enhancement of sapphires with the ultraviolet curable SU8 polymer surface structures consisting of conical subwavelength gratings (SWGs) at one- and both-side surfaces for different periods. The SWGs patterns on the silicon templates were transferred into the SU8 polymer film surface on sapphires by a simple and cost-effective soft lithography technique. For the fabricated samples, the surface morphologies, wetting behaviors, and optical characteristics were investigated. For theoretical optical analysis, a rigorous coupled-wave analysis method was used. At a period of 350 nm, the sample with SWGs on SU8 film/sapphire exhibited a hydrophobic surface and higher total transmittance compared to the bare sapphire over a wide wavelength of 450-1000 nm. As the period of SWGs was increased, the low total transmittance region of < 85% was shifted towards the longer wavelengths and became broader while the diffuse transmittance was increased (i.e., larger haze ratio). For the samples with SWGs at both-side surfaces, the total and diffuse transmittance spectra were further enhanced compared to the samples with SWGs at one-side surface. The theoretical optical calculation results showed a similar trend to the experimentally measured data.