Additive-assisted control over phase-separated nanostructures by manipulating alkylthienyl position at donor backbone
Jianhua Huang1, Xue Wang, Xin Zhang
1Beijing National Laboratory for Molecular Sciences, CAS Key Laboratory of Photochemistry, Institute of Chemistry, Chinese Academy of Sciences , Beijing 100190, P. R. China .
Abstract:
A non-fullerene, all-small-molecule solar cell (NF-SMSC) device uses the blend of a small molecule donor and a small molecule acceptor as the active layer. Aggregation ability is a key factor for this type of solar cell. Herein, we used the alkylthienyl unit to tune the aggregation ability of the diketopyrrolopyrrole (DPP)-based small molecule donors. Replacing two alkoxyl units in BDT-O-DPP with two alkylthienyl units yields BDT-T-DPP, and further introducing another two alkylthienyl units into the backbone produces BDT-T-2T-DPP. With the introduction of alkylthienyl, the backbone becomes twisted. As a result, the ππ-stacking strength, aggregation ability, and crystallite size all obey the sequence of BDT-O-DPP > BDT-T-DPP > BDT-T-2T-DPP. When selected a reported perylene diimide dimer of bis-PDI-T-EG as acceptor, the best NF-SMSC device exhibits a power conversion efficiency of 1.34, 2.01, and 1.62%, respectively, for the BDT-O-DPP, BDT-T-DPP, and BDT-T-2T-DPP based system. The BDT-T-DPP/bis-PDI-T-EG system yields the best efficiency of 2.01% among the three combinations. This is due to the moderate aggregation ability of BDT-T-DPP yields moderate phase size of 30-50 nm, whereas the strong aggregation ability of BDT-O-DPP gives a bigger size of 50-80 nm, and the weak aggregation ability of BDT-T-2T-DPP produces a smaller size of 10-30 nm. The BDT-T-DPP/bis-PDI-T-EG combination exhibits balanced hole/electron mobility of 0.022/0.016 cm(2)/(V s), whereas the BDT-O-DPP/bis-PDI-T-EG and the BDT-T-2T-DPP/bis-PDI-T-EG blend show a hole/electron mobility of 0.0011/0.0057 cm(2)/(V s) and 0.0016/0.11 cm(2)/(V s), respectively.