Effect of Ising-type Tb3+ ions on the low-temperature magnetism of La, Ca cobaltite

Crystal and magnetic structures of the x = 0.2 member of the La0.8-xTbxCa0.2CoO3 perovskite series have been determined from powder neutron diffraction. Enhancement of the diffraction peaks due to ferromagnetic or cluster glass ordering is observed below TC = 55 K. The moments first evolve on Co sites, and ordering of Ising-type Tb(3+) moments is induced at lower temperatures by a molecular field due to Co ions. The final magnetic configuration is collinear Fx for the cobalt subsystem, while it is canted FxCy for terbium ions. The rare-earth moments align along local Ising axes within the ab-plane of the orthorhombic Pbnm structure. The behavior in external fields up to 70-90 kOe has been probed by magnetization and heat capacity measurements. The dilute terbium ions contribute to significant coercivity and remanence that both steeply increase with decreasing temperature. A remarkable manifestation of the Tb(3+) Ising character is the observation of a low-temperature region with an anomalously large linear term of heat capacity and its field dependence. Similar behaviors are detected also for other terbium dopings x = 0.1 and 0.3.