Utilizing dynamic annealing during ion implantation: synthesis of silver nanoparticles in crystalline lithium niobate

Silver nanoparticles (NPs) embedded in lithium niobate were fabricated via ion beam synthesis and are suitable for various plasmonic applications, e.g. enhancement of optical nonlinear effects. After room temperature silver implantation, annealing in the temperature range of 400-600 °C was performed in order to recrystallize the damaged lithium niobate surface layer. The shape of the silver NPs, their optical properties as well as the structural properties of their surrounding matrix have been analyzed for various annealing steps. TEM investigations show that annealing at 400 °C does not lead to recrystallization of the damaged lithium niobate. A recrystallization occurs upon increasing the annealing temperature to 500 or 600 °C, but simultaneously a second phase consisting of lithium triniobate forms. This is additionally supported by XRD measurements. By utilizing dynamic annealing, i.e. implanting silver at elevated temperatures of 400 °C, it is shown that the LiNbO3 matrix stays single crystalline during ion implantation and no LiNb3O8 is formed. This is additionally verified by comparing the positions of the surface plasmon resonances with calculations based on Mie's scattering theory.