Effect of mild alkali pretreatment on structural changes of reed (Phragmites communis Trinius) straw

The effect of dilute sodium hydroxide (NaOH) on reed straw structural change at 105 degreeC temperature was evaluated in this study. Various concentrations of NaOH (1% to 2.5%) were used for pretreatment of reed straw at 105 degreeC for 10min. Scanning electron microscopy, atomic force microscopy and Fourier transform infrared spectroscopy studies showed that 2% and 2.5% NaOH pretreated sample exposed more cellulose fibers compared with other treatments. The cellulose crystalline index was increased by the 1% to 2.0% NaOH treatments and slightly lowered by the 2.5% NaOH treatment due to destructing cellulose fibres. Two per cent NaOH pretreatment caused 69.9% lignin removal, whereas 2.5% NaOH pretreatment removed 72.4% lignin. Besides, reed straw, when pretreated at 2% and 2.5% NaOH, resulted 56.4% and 60.5% hemicellulose removal, respectively. However, the difference in removal of lignin and hemicellulose between 2% and 2.5% NaOH treated reed straw was very marginal. In addition, very negligible increase of cellulose level was estimated, amounting 78.8% and 76.6% in 2.5% and 2% NaOH-treated sample, respectively. Moreover, after 72 h, reducing sugar yield was 81.2% and 83.3% using enzyme loading of 15 FPU (g dry biomass)-' and 30 IU (g dry biomass)- and xylanase 4 FXU (g dry biomass)-1 from 2% and 2.5% NaOH pretreated reed straw, respectively. Reducing sugar yield was increased very marginally when NaOH concentration increased from 2% to 2.5% for reed straw pretreatment. Therefore, 2% NaOH is supposed to be effective for reed straw pretreatment at this mentioned condition.