Microtensile bond strength between indirect composite resin inlays and dentin: effect of cementation strategy and...

To evaluate the microtensile bond strength of indirect resin composite inlays to dentin using two cementation strategies, before and after mechanical aging.

Standardized inlay cavities (bucco-lingual width: 3 mm; depth: 4 mm) were prepared in 32 human premolars. The teeth were embedded in self-curing acrylic resin up to 3 mm from the cementoenamel junction, impressions were made using a polyvinyl siloxane material, master dies were obtained using type 4 stone, and inlay composite resin restorations were fabricated (Sinfony, 3M ESPE). The teeth were randomly allocated into 4 groups according to the cementation strategy (conventional [C] and simplified [S]) and aging (mechanical cycling [MC] and not aged): C[G1]: Adper SingleBond + RelyX ARC without aging; CMC[G2]: conventional cementation + mechanical cycling (106 cycles, 88 N, 4 Hz, ± 37°C); S[G3]: self-adhesive resin cement (RelyX U-100) without aging; SMC[G4] self-adhesive cementation + mechanical cycling. Intaglio surfaces of composite inlays were treated by tribochemical silica coating in G1 and G2, while G3 and G4 received no surface treatment. Non-aged specimens were stored in a moist environment at ca 37°C for the same period as MC (3 days). Non-trimmed beam specimens (bonding area = 1 mm²) were produced by serial cutting, and microtensile testing was performed (0.5 mm/min).

Two-way ANOVA showed that the microtensile bond strength was affected only by cementation strategy (p < 0.0001). Tukey's test showed that groups G1 (35.1 ± 9.1) and G2 (32.7 ± 10.7) presented significantly higher bond strength values than G3 (8.7 ± 6.3) and G4 (5.2 ± 4.6).

The use of a conventional adhesive technique and tribochemical silica coating resulted in higher μTBS than the one-step simplified cementation, even after mechanical cycling.