Charge trapping at the step edges of TiO(2) anatase (101)

A combination of photoemission, atomic force, and scanning tunneling microscopy/spectroscopy measurements shows that excess electrons in the TiO2 anatase (101) surface are trapped at step edges. Consequently, steps act as preferred adsorption sites for O2 . In density functional theory calculations electrons localize at clean step edges, this tendency is enhanced by O vacancies and hydroxylation. The results show the importance of defects for the wide-ranging applications of titania.