Crystal growth, structural, electrical, and magnetic properties of mixed-valent compounds YbOs2Al10 and LuOs2Al10

Single crystals of YbOs2Al10 and LuOs2Al10 were grown for the first time using an aluminum self-flux method. The compounds crystallized into a cagelike structure in space group Cmcm, similar to the prototype compound YbFe2Al10. YbOs2Al10 exhibited a mixed-valent nature, as determined by magnetic susceptibility measurements over a wide temperature range from 2 to 900 K, in which the inter-configuration-fluctuation model revealed a broad peak around 400 K. In contrast, LuOs2Al10 displayed Pauli-like paramagnetic behavior over the same temperature range. Both compounds were metallic in nature between 2 and 300 K. The electronic specific heat coefficient of 21.3(2) mJ mol(-1) K(-2) for YbOs2Al10 was determined to be larger than that for LuOs2Al10 [8.9(1) mJ mol(-1) K(-2)], reflecting the mixed-valent nature of the former. First-principles calculations predicted the presence of a mixed-valent state in YbOs2Al10, in agreement with the experimental observations. The novel compound YbOs2Al10 elucidates the evolution of the mixed-valent nature of the Yb-based ternary transition metal aluminides from the 3d to 5d elements.