Synthesis of superparamagnetic bare Fe₃O₄ nanostructures and core/shell (Fe₃O₄/alginate) nanocomposites

In this article we report about the synthesis of superparamagnetic bare Fe3O4 nanostructures and core/shell (Fe3O4/alginate) nanocomposites by simple low-temperature based method at pH values 5, 9, and 14. The structural morphology and magnetic behavior of Fe3O4 nanostructures and core/shell (Fe3O4/alginate) nanocomposites (Fe3O4/alg NCs) have been investigated by X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy (RS), ultraviolet-visible (UV-vis) spectroscopy, transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX) and vibrating sample magnetometer (VSM). The particle size was calculated by TEM measurements and it turns out to be ∼10 nm and ∼14 nm for bare Fe3O4 nanoparticle and Fe3O4/alg NCs with core/shell structure, respectively. The magnetic properties of the synthesized products were found to be function of pH at which the synthesis has been done. The synthesized Fe3O4 nanoparticle and Fe3O4/alg NCs were found to be superparmagnetic in nature at room temperature. We observed that the value of saturation magnetization in case of Fe3O4/alg NCs decreases by increasing the pH value.