Electromechanical characterization of [Formula: see text] crystals as a function of crystallographic orientation and...

Relaxor based [Formula: see text] ternary single crystals (PIN-PMN-PT) were reported to have broader temperature usage range [Formula: see text] and comparable piezoelectric properties to [Formula: see text] (PMNT) crystals. In this work, the orientation dependent dielectric, piezoelectric and electromechanical properties for PIN-PMN-PT crystals were investigated along [Formula: see text] and [Formula: see text] directions. The electromechanical couplings [Formula: see text] and [Formula: see text] for [Formula: see text] poled crystals were found to be 0.91 and 0.91, respectively, with piezoelectric coefficients [Formula: see text] and [Formula: see text] on the order of 925 and -1420 pC/N. Of particular significance was the mechanical quality factor [Formula: see text] for [Formula: see text] oriented crystals, which was found to be [Formula: see text], much higher than the [Formula: see text] values of [Formula: see text] oriented relaxor-PT crystals [Formula: see text]. The temperature dependence of the piezoelectric properties exhibited good temperature stability up to their ferroelectric phase transition [Formula: see text], indicating [Formula: see text] and [Formula: see text] oriented PIN-PMN-PT are promising materials for transducer applications, with the latter for high power resonant devices where low loss (high [Formula: see text]) was required.