dependence of melt behavior of star polystyrene/POSS composites on the molecular weight of arm chains

Haiying Tan1, Jun Zheng, Donghua Xu

  • 1State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences , Changchun 130022, China.

The Journal of Physical Chemistry. B
|April 24, 2014
PubMed

More Related Videos

Using Polystyrene-block-polyacrylic acid-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization09:02

Using Polystyrene-block-polyacrylic acid-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization

Published on: July 9, 2015

10.2K
Solution Blow Spinning of Polymeric Nano-Composite Fibers for Personal Protective Equipment07:08

Solution Blow Spinning of Polymeric Nano-Composite Fibers for Personal Protective Equipment

Published on: March 18, 2021

3.1K

Related Concept Videos

Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
2.3K
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
2.1K
Polymers: Defining Molecular Weight01:01

Polymers: Defining Molecular Weight

Unlike small molecules with definite molecular weights, polymers are a mixture of individual polymer chains of varying lengths, each with a unique molecular weight. So, the molecular weight of a polymer is expressed as an average value based on the average size of the polymer chains. The two most common forms of averages used for polymers are the number average molecular weight and weight average molecular weight.
The number average molecular weight (Mn) is the summation of the number...
3.0K
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.
4.0K
Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
2.9K
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
3.1K