Free radical entrapment and crystallinity of resin composites after accelerated aging as a function of the expiration

Paulo Henrique Perlatti D'Alpino1, Marcos Vinícius Gonçalves Vismara2, Alejandra Hortencia Miranda González1

  • 1Biomaterials Research Group, School of Dentistry, Anhanguera University of São Paulo - UNIAN SP, São Paulo, SP, Brazil.

Journal of the Mechanical Behavior of Biomedical Materials
|May 13, 2014
PubMed

Keywords:
AgingComposite resinsEPRMethacrylateSiloraneStorage temperatureX-ray diffraction

More Related Videos

Stereolithographic 3D Printing with Renewable Acrylates08:28

Stereolithographic 3D Printing with Renewable Acrylates

Published on: September 12, 2018

9.1K
Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

13.3K

Related Concept Videos

Radical Autoxidation01:20

Radical Autoxidation

The oxidation of an organic compound in the presence of air or oxygen is called autoxidation. For example, cumene reacts with oxygen to form hydroperoxide. Autoxidation involves initiation, propagation, and termination steps. Many organic compounds are susceptible to autoxidation—especially ethers in the presence of oxygen, which form hydroperoxides. Even though this reaction is slow, old ether bottles contain small amounts of peroxide, which leads to laboratory explosions during ether...
2.5K
Radical Chain-Growth Polymerization: Chain Branching01:17

Radical Chain-Growth Polymerization: Chain Branching

The skeletal structure of polymers synthesized via radical polymerization is always branched. For example, the polymerization of ethylene by radical polymerization results in a low-density grade of polyethylene with a heavily branched skeletal structure. Here, the radical site abstracts hydrogen from the growing chain, and the radical site shifts from the end (a primary carbon center) to anywhere within the growing chain (a secondary carbon center). Consequently, the part of the chain from the...
1.8K
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
3.1K
Radical Reactivity: Steric Effects01:10

Radical Reactivity: Steric Effects

The presence of electron-donating, electron-withdrawing, or conjugating groups adjacent to a radical center, imparts electronic stabilization to the radicals. Examples of such electronically-stabilized radicals are triphenylmethyl, tetramethylpiperidine‐N‐oxide, and 2,2‐diphenyl‐1‐picrylhydrazyl. These radicals are remarkably stable and are known as persistent radicals. Some of the persistent radicals can even be isolated and purified.
Along with electronic...
1.6K
Autoxidation of Ethers to Peroxides and Hydroperoxides02:23

Autoxidation of Ethers to Peroxides and Hydroperoxides

Ethers represent a class of chemical compounds that become more dangerous with prolonged storage because they tend to form explosive peroxides when standing in the air. Autoxidation is the spontaneous oxidation of a compound in air. In the presence of oxygen, ethers slowly oxidize to form hydroperoxides and dialkyl peroxides.
8.2K
Radical Chain-Growth Polymerization: Overview01:10

Radical Chain-Growth Polymerization: Overview

Chain-growth or addition polymerization is successive addition reactions of monomers with a polymer chain. In radical chain-growth polymerization, the reaction proceeds via a free-radical intermediate. The free radical is formed from radical initiators, which spontaneously generate free radicals by homolytic fission. Organic peroxides (such as dibenzoyl peroxide, as shown in Figure 1) or azo compounds are popular radical initiators. A low concentration ratio of radical initiator to monomer is...
2.7K