Analysis of Contact Interfaces for Single GaN Nanowire Devices
Published on: November 15, 2013
Direct imaging of p-n junction in core-shell GaN wires
P Tchoulfian1, F Donatini, F Levy
1Univ. Grenoble Alpes , F-38000 Grenoble, France.
Abstract:
While core-shell wire-based devices offer a promising path toward improved optoelectronic applications, their development is hampered by the present uncertainty about essential semiconductor properties along the three-dimensional (3D) buried p-n junction. Thanks to a cross-sectional approach, scanning electron beam probing techniques were employed here to obtain a nanoscale spatially resolved analysis of GaN core-shell wire p-n junctions grown by catalyst-free metal-organic vapor phase epitaxy on GaN and Si substrates. Both electron beam induced current (EBIC) and secondary electron voltage constrast (VC) were demonstrated to delineate the radial and axial junction existing in the 3D structure. The Mg dopant activation process in p-GaN shell was dynamically controlled by the ebeam exposure conditions and visualized thanks to EBIC mapping. EBIC measurements were shown to yield local minority carrier/exciton diffusion lengths on the p-side (∼57 nm) and the n-side (∼15 nm) as well as depletion width in the range 40-50 nm. Under reverse bias conditions, VC imaging provided electrostatic potential maps in the vicinity of the 3D junction from which acceptor Na and donor Nd doping levels were locally determined to be Na = 3 × 10(18) cm(-3) and Nd = 3.5 × 10(18) cm(-3) in both the axial and the radial junction. Results from EBIC and VC are in good agreement. This nanoscale approach provides essential guidance to the further development of core-shell wire devices.
Related Concept Videos
P-N junction
Biasing of P-N Junction
In equilibrium, no external voltage is applied across the p-n junction. The depletion region is formed at the junction interface due to the diffusion of carriers, which leaves behind charged dopants, acceptors on the p-side, and donors on the n-side. These immobile charges create an electric field that prevents further diffusion of carriers. The related energy band...
Metal-Semiconductor Junctions
Schottky Barriers
Schottky barriers arise when a metal with a work function (Φm) contacts a semiconductor with a different work function (Φs). Initially, electrons transfer until the Fermi levels of the metal and semiconductor align at equilibrium. For instance, if Φm > Φs, the semiconductor Fermi level is higher than the metal's before contact. The...
Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
Schottky Barrier Diode
Semiconductors
Metals such as copper (Cu), zinc (Zn), or lead (Pb) have low resistivity and feature conduction bands that are either not fully occupied or overlap with the valence band, making a bandgap non-existent. This allows electrons in the highest energy levels of the valence band to easily transition to the conduction band upon gaining...