Effect of fluoride content on ion release from cast and selective laser melting-processed Co-Cr-Mo alloys
Xu Yang1, Nan Xiang2, Bin Wei3
1Postgraduate student, Department of Prosthodontics, Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai Key Laboratory of Stomatology, Department of Prosthodontics, Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai Key Laboratory of Stomatology, Shanghai, China.
Statement Of Problem:
Selective laser melting (SLM) alloy is gaining popularity in prosthetic dentistry. However, its biocompatibility has been of some concern because of long-term exposure to fluoride in the oral environment.
Purpose:
The purpose of this study was to examine the effect of fluoride concentration on ion release from Co-Cr-Mo alloy specimens fabricated using either SLM or lost-wax casting when immersed in an artificial saliva solution containing fluoride.
Material And Methods:
Specimens were prepared with either a SLM system for the SLM alloy or conventional lost-wax techniques for the cast alloy. The specimen surfaces were wet ground with silicon carbide paper (400, 800, and 1200 grit) and immersed in modified artificial saliva solutions, the pH of which had been adjusted to 5.0 with lactic acid and which contained NaF at concentrations of 0.00%, 0.05%, 0.1%, or 0.2%. The metal ion content of the solution was determined with an inductively coupled plasma mass spectrometer. The results were submitted to 2-way ANOVA and regression analysis (α=.05).
Results:
Fluoride concentration significantly influenced the elemental ion release from both the SLM and cast alloys. The quantity of ions released increased significantly with increasing fluoride concentration. The ion release from the cast specimens was significantly greater than that from the SLM specimens.
Conclusions:
The performance of the SLM alloy in immersion tests demonstrates that this new technique is a superior choice because of its good biocompatibility.
More Related Videos
08:55Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses
Published on: June 7, 2018
09:22Casting Protocols for the Production of Open Cell Aluminum Foams by the Replication Technique and the Effect on Porosity
Published on: December 11, 2014