Thermoluminescence of mercaptoethanol-capped ZnS:Mn nanoparticles

The thermoluminescence (TL) of nanoparticles has become a matter of keen interest in recent times but is rarely reported. This article reports the synthesis of ZnS:Mn nanocrystals using a chemical route, with mercaptoethanol (ME) as the capping agent. The particle sizes for the nanocrystals were measured by X-ray diffraction (XRD) and also by studying transmission electron microscopy (TEM) patterns. The particle sizes of the synthesized samples were found to be between 1 and 3 nm. For samples with different concentrations of the capping agent, it was found that the TL intensity of the ZnS:Mn nanoparticles increased as the particle size decreased. A shift in the peak position of the TL glow curve was also seen with decreasing particle size. The TL intensity was found to be maximal for samples with 1.2% of Mn. A change in the peak position was not found for samples with different concentrations of Mn. The half-width glow peak curve method was used to determine the trap-depth. The frequency factor of the synthesized samples was also calculated. The stability of the charge carriers in the traps increases with decreasing nanoparticle size. The higher stability may be attributed to the higher surface/volume ratio and also to the increase in the trap-depth with decreasing particle size.