High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels
Published on: April 16, 2017
Chromatographycally efficient microspherical composites of molecularly imprinted xerogels deposited inside mesoporous
Porkodi Kadhirvel1, Manuel Azenha1, A Fernando Silva1
1Centro de Investigação em Química and Faculdade de Ciências, University of Porto, 4169 007 Porto, Portugal.
Abstract:
A different approach to the preparation of microspheric particles of molecularly imprinted xerogels (MIX) is presented here. The technique consisted of filling up the pores of spherical, mesoporous, bare silica particles with a pregelification mixture by applying pressure. Upon gelification and drying, thin layers of MIX were deposited on the mesopores. Spherical composites of S-naproxen (S-NAP) imprints were produced by following this simple strategy. The performance of the imprints was quite satisfactory in terms of recognition ability (ascertained by selectivity against ibuprofen, α=4.9, and an imprinting factor of 13) whereas an outstanding improvement on dynamic features (expressed as column efficiency), as compared to the corresponding bulk format MIX (9 vs. 1.2 theoretical plates/cm), was reached.