Mediator enhanced water oxidation using Rb4[Ru(II)(bpy)3]5[{Ru(III)4O4(OH)2(H2O)4}(γ-SiW10O36)2] film modified...

The water insoluble complex Rb4[Ru(II)(bpy)3]5[{Ru(III)4O4(OH)2(H2O)4}(γ-SiW10O36)2], ([Ru(II)bpy]5[Ru(III)4POM]), was synthesized from Rb8K2[{Ru(IV)4O4(OH)2(H2O)4}(γ-SiW10O36)2] and used for electrocatalytic water oxidation under both thin- and thick-film electrode conditions. Results demonstrate that the [Ru(II)bpy]5[Ru(III)4POM] modified electrode enables efficient water oxidation to be achieved at neutral pH using thin-film conditions, with [Ru(bpy)3](3+)([Ru(III)bpy]) acting as the electron transfer mediator and [Ru(V)4POM] as the species releasing O2. The rotating ring disc electrode (RRDE) method was used to quantitatively determine the turnover frequency (TOF) of the catalyst, and a value of 0.35 s(-1) was obtained at a low overpotential of 0.49 V (1.10 V vs Ag/AgCl) at pH 7.0. The postulated mechanism for the mediator enhanced catalytic water process in a pH 7 buffer containing 0.1 M LiClO4 as an additional electrolyte includes the following reactions (ion transfer for maintaining charge neutrality is omitted for simplicity): [Ru(II)bpy]5[Ru(III)4POM] → [Ru(III)bpy]5[Ru(V)4POM] + 13 e(-) and [Ru(III)bpy]5[Ru(V)4POM] + 2H2O → [Ru(III)bpy]5[Ru(IV)4POM] + O2 + 4H(+). The voltammetry of related water insoluble [Ru(II)bpy]2[S2M18O62] (M = W and Mo) and [Fe(II)Phen]x[Ru(III)4POM] materials has also been studied, and the lack of electrocatalytic water oxidation in these cases supports the hypothesis that [Ru(III)bpy] is the electron transfer mediator and [Ru(V)4POM] is the species responsible for oxygen evolution.