Films loaded with insulin-coated nanoparticles (ICNP) as potential platforms for peptide buccal delivery

The goal of this investigation was to develop films containing insulin-coated nanoparticles and evaluate their performance in vitro as potential peptide delivery systems. To incorporate insulin into the films, a new antisolvent co-precipitation fabrication process was adapted to obtain insulin-coated nanoparticles (ICNPs). The ICNPs were embedded in polymeric films containing a cationic polymethacrylate derivative (ERL) or a combination of ERL with hydroxypropyl methylcellulose (HPMC). ICNP-loaded films were characterized for morphology, mucoadhesion, and insulin release. Furthermore, in vitro insulin permeation was evaluated using a cultured tridimensional human buccal mucosa model. The antisolvent co-precipitation method was successfully adapted to obtain ICNPs with 40% (w/w) insulin load, achieving 323±8nm particles with a high zeta potential of 32.4±0.8mV, indicating good stability. High yields were obtained after manufacture and the insulin content did not decrease after one month storage. ICNP-embedded films using ERL as the polymer matrix presented excellent mucoadhesive and insulin release properties. A high permeation enhancement effect was observed for ICNP-loaded ERL films in comparison with ICNP-loaded ERL-HPMC films and a control insulin solution. ICNP-loaded ERL formulations were found to be more effective in terms of film performance and insulin permeation through the human buccal mucosa model, and thus are a promising delivery system for buccal administration of a peptide such as insulin.