Engineering scaffolds integrated with calcium sulfate and oyster shell for enhanced bone tissue regeneration

Engineering scaffolds combinging natural biomineral and artificially synthesized material hold promising potential for bone tissue regeneration. In this study, novel bioactive calcium sulfate/oyster shell (CS/OS) composites were prepared. Comparing to CS scaffold, the CS/OS composites with a controllable degradation rate displayed enhanced mineral nodule formation, higher alkaline phosphate (ALP) activity and increased proliferation rate while treated osteocytes. In CS/OS composites group, elevated mRNA levels of key osteogenic genes including bone morphogenetic protein-2 (BMP-2), runt-related transcription factor 2 (Runx2), osterix (Osx), and osteocalcin (OCN) were observed. Furthermore, The up-regulation of BMP-2 and type I collagen (COL-I) was observed for CS/OS composites relative to a CS group. Scaffolds were implanted into critical-sized femur cavity defects in rabbits to investigate the osteogenic capacity of the composites in vivo. The CS/OS scaffolds with proper suitable times and mechanical strength strongly promoted osteogenic tissue regeneration relative to the regeneration capacity of CS scaffolds, as indicated by the results of histological staining. These results suggest that the OS-modified CS engineering scaffolds with improved mechanical properties and bioactivity would facilitate the development of a new strategy for clinic bone defect regeneration.