Surface dynamics of poly(methyl methacrylate) films affected by the concentration of casting solutions
Houkuan Tian1, Yuhui Yang, Jia Ding
1Department of Chemistry, Key Laboratory of Advanced Textile Materials and Manufacturing Technology of the Education Ministry, Zhejiang Sci-Tech University, Hangzhou 310018, China. wxinping@yahoo.com wxinping@zstu.edu.cn.
Abstract:
The effect of the concentration of casting solutions on the surface dynamics of the corresponding spin-coated poly(methyl methacrylate) (PMMA) film was investigated by measuring the surface reorganization of fluorine tracer-labeled PMMA. The onset temperature of fluorinated PMMA chain end reorganization (T(onsetR)) was identified and is shown to depend on the PMMA concentration in the film-forming solution. It was found that the surface T(onsetR) and relaxation activation energy E(a) of the PMMA films prepared from 4.2 wt% PMMA cyclohexanone solution are 70 °C and 260 kJ mol(-1), respectively, which are higher than those of the PMMA films prepared from 0.8 wt% PMMA cyclohexanone solution (55 °C and 144 kJ mol(-1), respectively). The T(onsetR) and E(a) of PMMA films increased with increasing concentration of casting solutions within the range of 1.8 wt% to 4 wt%. The chain entanglement of PMMA chains is proposed to be the speculative origin for these observed depressed dynamics of poly(methyl methacrylate) chains on the films' surface prepared using casting solutions of various concentrations.