Cyclic fatigue resistance of nickel-titanium instruments after immersion in irrigant solutions with or without
Eugenio Pedullà1, Giovanni Franciosi2, Hani F Ounsi2
1Department of Surgery, University of Catania, Catania, Italy.
Introduction:
The aim of the study was to assess cyclic fatigue resistance of reciprocating (Reciproc and WaveOne) and continuous rotating (ProTaper) nickel-titanium files after immersion in different irrigation solutions with or without surfactants during several short time periods.
Methods:
A total of 270 new Reciproc R25, WaveOne Primary, and ProTaper F2 files were tested. Instruments of each brand were divided into 1 control group (n = 10) formed by new files and 4 test groups (n = 20) formed by instruments dynamically immersed at 37°C for 16 mm in 5.25% sodium hypochlorite (NaOCl), Hypoclean (5.25% NaOCl with surfactant), 17% EDTA, or EDTA Plus (17% EDTA with surfactant). Each test group was subdivided into 2 subgroups (n = 10) on the basis of the time of dynamic immersion in the endodontic irrigant solution (45 seconds or 3 minutes). Resistance to cyclic fatigue was determined by recording time to fracture in a stainless steel artificial canal with a 60° angle of curvature and 5-mm radius of curvature. The fracture surface was examined by using scanning electron microscopy.
Results:
Immersion in NaOCl did not reduce the cyclic fatigue of reciprocating or continuous nickel-titanium files. The 17% EDTA reduced the fatigue resistance of all instruments after 3 minutes. The immersion in irrigants with surfactants did not influence the cyclic fatigue of instruments except for Reciproc immersed in Hypoclean solution.
Conclusions:
EDTA immersion reduced the cyclic fatigue resistance of all instruments after 3 minutes. Addition of surfactants did not influence the cyclic fatigue of files except when added to NaOCl when it contacts Reciproc instruments.