Effects of multipurpose, universal adhesives on resin bonding to zirconia ceramic

This study evaluated the effects of single-bottle, multipurpose, universal adhesives on the bond strength of resin cement to zirconia ceramic. Polished zirconia ceramic (Cercon base) discs were randomly divided into four groups (n=40) according to the applied surface-conditioning agent: Single Bond 2, Single Bond Universal, All-Bond Universal, and Alloy Primer. Cured composite cylinders (Ø 0.8 mm × 1 mm) were cemented to the conditioned zirconia specimens with resin cement (RelyX ARC). The bonded specimens were subjected to a microshear bond-strength test after 24 hours of water storage and after 10,000 cycles of thermocycling. The surface-conditioning agent significantly influenced the bond strength (p<0.05). Single Bond Universal showed the highest initial bond strength (37.7 ± 5.1 MPa), followed by All-Bond Universal (31.3 ± 5.6 MPa), Alloy Primer (26.9 ± 5.1 MPa), and Single Bond 2 (8.5 ± 4.6 MPa). Artificial aging significantly reduced the bond strengths of all the test groups (p<0.05). After 10,000 cycles of thermocycling, All-Bond Universal showed the highest bond-strength value (26.9 ± 6.4 MPa). Regardless of artificial aging, Single Bond Universal and All-Bond Universal showed significantly higher bond strengths than Alloy Primer, a conventional metal primer.