Polymerization shrinkage and depth of cure of bulk-fill resin composites and highly filled flowable resin

J-H Jang, S-H Park, I-N Hwang

    Operative Dentistry
    |August 20, 2014
    PubMed

    More Related Videos

    Stereolithographic 3D Printing with Renewable Acrylates08:28

    Stereolithographic 3D Printing with Renewable Acrylates

    Published on: September 12, 2018

    9.1K
    Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials05:30

    Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials

    Published on: January 10, 2025

    1.1K

    Related Concept Videos

    Shrinkage in Concrete01:27

    Shrinkage in Concrete

    Shrinkage in concrete is primarily due to water loss from evaporation, hydration of cement, or carbonation, leading to a reduction in volume. The volumetric contraction results in volumetric strain in concrete. However, in practice, shrinkage is measured as linear strain, which is one-third of the volumetric strain.
    When concrete is still in its plastic state, it can undergo a decrease in volume by about 1% of its absolute volume. This decrease is known as plastic shrinkage. It arises either...
    591
    Drying Shrinkage01:21

    Drying Shrinkage

    When hardened concrete is exposed to air with a relative humidity of less than 100 percent, it begins to lose the free water within its capillaries. As this water evaporates, the water initially adsorbed onto the calcium silicate hydrates migrates towards these now empty spaces and eventually evaporates as well. Over time, as more water leaves, the volume of the concrete decreases, a phenomenon known as drying shrinkage.
    A portion of this drying shrinkage can be reversed; if the concrete is...
    517
    Polymer Classification: Crystallinity01:21

    Polymer Classification: Crystallinity

    Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
    Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
    3.1K
    Curing of Concrete01:20

    Curing of Concrete

    The hydration of cement takes place within the water-filled capillary pores. However, environmental elements can disrupt this process by evaporating water from the concrete surfaces. Sealed concrete with a water-cement ratio below 0.5 experiences self-desiccation, leading to water loss. The water loss in concrete is mitigated by curing. This technique involves keeping the concrete saturated to maintain the necessary temperature and moisture conditions, to optimally fill the spaces in the cement...
    1.4K
    Accelerated Curing of Concrete01:25

    Accelerated Curing of Concrete

    Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...
    648