Formation and sintering of Pt nanoparticles on vicinal rutile TiO₂ surfaces
Felix Rieboldt1, Stig Helveg, Ralf Bechstein
1Interdisciplinary Nanoscience Center (iNANO), Department of Physics and Astronomy, Aarhus University, DK-8000 Aarhus C, Denmark. swendt@phys.au.dk.
Abstract:
By means of scanning tunnelling microscopy (STM) the nucleation, growth and sintering of platinum nanoparticles (Pt NP's) was studied on vicinal and flat rutile titanium dioxide (TiO2) surfaces. Utilising physical vapour deposition, the nucleation of Pt NP's on TiO2 surfaces at room temperature (RT) was found to be random and invariant towards different surface morphologies and reduction states. Thus, the nucleation of Pt on TiO2 at RT is rather insensitive to the surface structure and surface defects. Vacuum-annealing at 600 K, 700 K and 800 K, respectively, led to lower densities of Pt NP's as a result of sintering. Sintering occurred at different rates at the TiO2 surfaces studied, indicating that the surface morphology and the amount of Ti(3+) excess charge do have an influence on the particle stability. Observed changes in the NP distribution as a result of sintering can be explained inferring facile diffusion of Pt NP's along the [001] direction.