Sulfurization induced surface constitution and its correlation to the performance of solution-processed...

To obtain high photovoltaic performances for the emerging copper zinc tin sulfide/selenide (CZTSSe) thin film solar cells, much effort has deservedly been placed on CZTSSe phase purification and CZTSSe grain size enhancement. Another highly crucial but less explored factor for device performance is the elemental constitution of CZTSSe surface, which is at the heart of p-n junction where major photogenerated carriers generate and separate. In this work we demonstrate that, despite the well-built phase and large grained films are observed by common phases and morphology characterization (XRD, Raman and SEM), prominent device efficiency variations from short circuited to 6.4% are obtained. Insight study highlights that the surface (0-250 nm) compositions variation results in different bulk defect depths and doping densities in the depletion zone. We propose that suitable sulfurization (at ~ 10 kPa sulfur pressure) drives optimization of surface constitution by managing the Cu, Zn and Sn diffusion and surface reaction. Therefore, our study reveals that the balance of elemental diffusion and interface reactions is the key to tuning the surface quality CZTSSe film and thus the performance of as resulted devices.